OK Aristorod 69 (ER110S-G) Гагнуурын утас / ESAB
Esab, Даацын гангийн утас / Tensile Steel / High Tensile Steel, Гагнуурын электрод болон утаснууд / Welding Consumables
OK Aristorod 69 (ER110S-G)
Стандарт:
SFA/AWS A5.28 ER110S-G
A low-alloyed, chromium-nickel-molybdenum (0,3% Cr, 1,4% Ni, 0,25% Mo), solid wire for GMAW of high tensile strength steels requiring tough weld metal for critical applications. Also suitable when high impact strength at lower temperatures is required.
Stoody 850 Хуяглалтын гагнуурын утас / ESAB
Esab, Хуяглалтын зориулалттай утас / Hard Facing, Гагнуурын электрод болон утаснууд / Welding Consumables
- Self Shielded (-O), Tubular Hardfacing Wire
- Air Hardening, Crack Prone High Carbon, Martensitic Steel Deposit
- Resistant to Severe Abrasion and Low Impact Loading
- 1.2mm size can be used for vertical surfacing by depositing overlapping horizontal stringer passes
Stoody 965 Хуяглалтын гагнуурын утас / ESAB
Esab, Хуяглалтын зориулалттай утас / Hard Facing, Гагнуурын электрод болон утаснууд / Welding Consumables
- Gas (-G) and Self Shielded (-O), Tubular Hardfacing WiresAir Hardening, Crack Free, Martensitic Steel Deposit
- Resistant to Hard Particle Abrasion and Moderate Impact Loading
- 1.2mm and 1.6mm sizes can be used for vertical surfacing by depositing overlapping horizontal stringer passes
- 1.2mm and 1.6mm wires are B5 type wires which require a shielding gas
- 2.4mm size is a B7 type open arc wire which requires no shielding gas
ESAB ШИРЭМНИЙ ЭЛЕКТРОД / OK 92.18
OK 92.18
SMAW
Type Basic-special, high graphite
A nickel-cored electrode for welding normal grades of cast iron. The weld metal is soft and easily machinable. Deposition is performed on cold or slightly preheated material. The electrode is suitable for the joining/repair of grey and malleable cast irons and the joining of these cast irons to steel, monel and copper.
Thin sections can be welded cold but it is recommended that preheat be used when welding thicker sections. When welding select the smallest diameter electrode practical and operate at low currents to keep dilution to a minimum. Stringer beads should be deposited using a stepped short run technique to avoid overheating of the workpiece.
During welding the joint can be lightly peened and on completion the workpiece should be allowed to cool slowly.
Welding current:
AC, DC+/- Min OCV 50 V